I’m pretty new to PETG, and have been really struggling with it compared to PLA. My latest print of this part is dimensionally accurate, but I need it to be air tight. It is very much not at the moment.
I have a Flashforge Adventurer 3, so the hot end and nozzle are one interchangeable unit. My higher temp nozzle is 0.6mm. My 0.3mm is only capable of 240. My last print was 0.2mm layers, with the 0.6mm nozzle at 245C. I used 15% overlap on my walls, and in order to keep my nice dimensions I had my cooling fan on.
Anybody have any advice on how to improve the seal? I’m tempted to try more overlap, with random start locations per layer. Do you think if I run it hotter I can get the layers a little thinner? Any advice would be appreciated.
100% agree with adding a coating agent after printing, but if you’re looking to minimize small holes and fissures, consistent line width is super important. High speeds can make thinner lines than when it slows down at starts/stops and corners.
Printing PETG slower than PLA is already a common recommendation, but unless your printer supports input shaping and linear (or pressure) advance, I’d go as slow as you can bear. As a perk, if 245 is the optimal temp for your usual speed, going slower will make 240 work better.
I’m not sure what my optimal temp is yet, I’ve been using 245 because it was the middle of the range recommended by my filament. I will definitely try slower, I had already slowed to 50% my PLA speed. I’ll try like 30% though!